Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.08 | kg·cm/cm(J/M)ft·lb/in |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 0.2 | % |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 30 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD | ASTMD955 | 0.40到0.60 | % |
| Melt mass flow rate | 220°C/10.0kg | ISO1133 | 30 | g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 31.4 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending modulus 3 | | ISO178 | 3700 | Mpa |
| Bending stress 3 | | ISO178 | 123 | Mpa |
| Tensile stress | 屈服 | ISO527-2/5 | 64.1 | Mpa |
| Bending modulus | | ASTM D790/ISO 178 | 3330(MPa) | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 97(MPa) | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Combustibility (rate) | | UL94 | HB | |
| Hot deformation temperature | | ASTM D648/ISO 75 | 90 | ℃（℉） |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 86.8 | °C |
| vicat softening point | | ASTM D1525/ISO R306 | 109 | ℃（℉） |
| Vicat softening temperature | | ISO306/B | 102 | °C |
| RTIElec | | UL746 | 50.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 50.0 | °C |
| RTI | | UL746 | 50.0 | °C |
| BallPressure Test4 | | EMAC | 95 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.