Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Shrinkage rate | MD1 | 内部方法 | 0.40到0.60 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.60 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| yield | | ISO527-2/50 | 59.0 | Mpa |
| crack | | ISO527-2/5 | 55.0 | Mpa |
| crack | | ISO527-2/50 | 59.0 | Mpa |
| yield | | ISO527-2/5,ISO527-2/50 | 4.0 | % |
| crack | | ISO527-2/5 | 120 | % |
| crack | | ISO527-2/50 | >50 | % |
| Bending modulus 2 | | ISO178 | 2400 | Mpa |
| Bending stress 3 | | ISO178 | 80.0 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 125 | mg |
| Tensile modulus | | ISO527-2/1 | 2500 | Mpa |
| yield | | ISO527-2/5 | 55.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| thermal conductivity | | ISO8302 | 0.20 | W/m/K |
| RTIElec | | UL746 | 50.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 50.0 | °C |
| RTI | | UL746 | 50.0 | °C |
| 0.45MPa, unannealed, 100mm span | | ISO75-2/Be | 125 | °C |
| 1.8MPa, unannealed, 100mm span | | ISO75-2/Ae | 101 | °C |
| -- | | ISO306/B50 | 119 | °C |
| -- | | ISO306/B120 | 120 | °C |
| BallPressure Test | 75°C | IEC60695-10-2 | Pass | |
| BallPressure Test | 105°C7 | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23到60°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Dielectric strength | 3.20mm,在油中 | IEC60243-1 | 17 | KV/mm |
| Relative permittivity | 1MHz | IEC60250 | 2.90 | |
| Dissipation factor | 1MHz | IEC60250 | 0.015 | |
| Leakage Trace Index | | IEC60112 | 175 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam gap 4 | 23°C | ISO179/1eA | 65 | kJ/m² |
| Suspended wall beam gap impact strength 5 | -30°C | ISO180/1A | 10 | kJ/m² |
| Suspended wall beam gap impact strength 5 | 23°C | ISO180/1A | 45 | kJ/m² |
| Impact strength of simply supported beam gap 4 | -30°C | ISO179/1eA | 10 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R计秤 | ISO2039-2 | 118 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 104 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.750mm | UL94 | HB | |
| UL flame retardant rating | 3.00mm | UL94 | HB | |
| Burning wire flammability index | 3.20mm | IEC60695-2-12 | 750 | °C |
| Extreme Oxygen Index | | ISO4589-2 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.