Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 饱和,23°C | ISO62 | 0.50 | % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.20 | % |
| Melt volume flow rate | 240°C/5.0kg | ISO1133 | 24.0 | cm3/10min |
| Density/specific gravity | 23°C | ISO1183 | 1.18 | g/cm³ |
| MeltViscosity3 | 260°C | ISO11443-A | 160 | Pa·s |
| Shrinkage rate 2 | TD:240°C,3.00mm | ISO2577 | 0.50to0.70 | % |
| Shrinkage rate 2 | MD:240°C,3.00mm | ISO2577 | 0.50to0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | 屈服,23°C | ISO527-2/50 | 60.0 | Mpa |
| Tensile stress | 断裂,23°C | ISO527-2/50 | 45.0 | Mpa |
| Tensile strain | 屈服,23°C | ISO527-2/50 | 3.5 | % |
| Tensile strain | 断裂,23°C | ISO527-2/50 | >40 | % |
| Tensile modulus | 23°C | ISO527-2/1 | 2700 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 92.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 82.0 | °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO11359-2 | 7.6E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| Vicat softening temperature | -- | ISO306/B50 | 95.0 | °C |
| Vicat softening temperature | -- | ISO306/B120 | 97.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.20 | |
| Relative permittivity | 23°C,1MHz | IEC60250 | 3.10 | |
| Leakage Trace Index | 解决方案A | IEC60112 | 350 | V |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 35 | KV/mm |
| Surface resistivity | | IEC60093 | 1E+16 | ohms |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dissipation factor | 23°C,100Hz | IEC60250 | 5E-03 | |
| Dissipation factor | 23°C,1MHz | IEC60250 | 6E-03 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Unscented Izod impact strength | 23°C | ISO180 | NoBreak | |
| Impact strength of cantilever beam gap | -30°C | ISO180/A | 10 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 35 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| UL flame retardant rating | 2.0mm | UL94 | 5VB | |
| UL flame retardant rating | 3.0mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.