Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 2.6 | g/10min |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 7.0-12.0 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ASTM D638/ISO 527 | 34 | kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638/ISO 527 | 37 | kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 3 | % |
| Tensile yield strength | 1/8",5mm/min | ASTM D-638 | 37 | Mpa |
| Tensile fracture strength | 1/8",5mm/min | ASTM D-638 | 34 | Mpa |
| Tensile yield elongation | 1/8",5mm/min | ASTM D-638 | 3 | % |
| Tensile strain at break | 1/8",5mm/min | ASTM D-638 | 100 | % |
| IZOD notch impact strength 73 ° F (23 ℃) | 1/8",23℃ | ASTM D-256 | 27 | KJ/m |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 27 | kg·cm/cm(J/M)ft·lb/in |
| Tensile elongation at break (elongation at break) | | ASTM D638/ISO 527 | 100 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| vicat softening point | | ASTM D1525/ISO R306 | 107 | ℃（℉） |
| Vicat softening point (120 ℃/10hr) | 1/8",50℃/hr | ASTM D-1525 | 107 | °C |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 200℃,3.8kg | ASTM D-1238 | 2.6 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.