Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD:4.00mm | 内部方法 | 0.40to0.60 | % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.40to0.60 | % |
| Shrinkage rate | 平行方向 | | 0.4-0.6 | % |
| Shrinkage rate | 垂直方向 | | 0.4-0.6 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO 527-1,-2 | 3300 | Mpa |
| Tensile yield stress | | ISO 527-1,-2 | 63 | Mpa |
| Tensile fracture stress | | ISO 527-1,-2 | 46 | Mpa |
| Tensile yield elongation | | ISO 527-1,-2 | 2 | % |
| Tensile strain at break | | ISO 527-1,-2 | 20 | % |
| Tensile modulus | | ISO527-2/1 | 3300 | Mpa |
| Tensile stress | 屈服 | ISO527-2/50 | 63.0 | Mpa |
| Tensile stress | 断裂 | ISO527-2/50 | 46.0 | Mpa |
| Tensile strain | 屈服 | ISO527-2/50 | 2.0 | % |
| Tensile strain | 断裂 | ISO527-2/50 | 20 | % |
| Bending modulus 2 | | ISO178 | 3200 | Mpa |
| Bending stress 2 | | ISO178 | 96.0 | Mpa |
| Bending modulus | | ISO 178 | 3200 | Mpa |
| bending strength | | ISO 178 | 96 | Mpa |
| Izod notched impact strength | 没缺口 | ISO 179 | NB | KJ/m |
| Izod notched impact strength | 带缺口 | ISO 179 | 12 | KJ/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | -，1.80MPa | ISO 75-1 | 84 | °C |
| Hot deformation temperature | -，0.45Mpa | ISO 75-2 | 94 | °C |
| vicat softening point | | ISO 306 | 97 | °C |
| Coefficient of linear expansion | 平行方向 | ISO 11359-2 | 0.6 | |
| Coefficient of linear expansion | 垂直方向 | ISO 11359-2 | 0.7 | |
| Flame retardancy | | UL94 | V-0 | |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 94.0 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 84.0 | °C |
| Vicat softening temperature | | ISO306/B50 | 97.0 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 6E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+16 | ohms |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | NoBreak | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.2mm | UL94 | V-0 | |
| UL flame retardant rating | 1.8mm | UL94 | 5VB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.