Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.04 | |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 1.8 | g/10min |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 19 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| tensile strength | | ASTM D638/ISO 527 | 485(6870) | kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 20 | % |
| Rockwell hardness | | ASTM D785 | R-110 | |
| Bending modulus | | ASTM D790/ISO 178 | 2700(38000) | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 780(11,000) | kg/cm²(MPa)[Lb/in²] |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 23(4.2) | kg·cm/cm(J/M)ft·lb/in |
| IZOD notch impact strength | | ASTM D256/ISO 179 | 26(4、8) | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Combustibility (rate) | | UL94 | 1/16“HB | |
| Hot deformation temperature | | ASTM D648/ISO 75 | 99(210) | ℃（℉） |
| Hot deformation temperature | | ASTM D648/ISO 75 | 88(190) | ℃（℉） |
| vicat softening point | | ASTM D1525/ISO R306 | 105(221) | ℃（℉） |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dry conditions | | | 于85°C下烘料约3~4小时 | |
| Mold temperature | | | 30~70°C | °C |
| Processing temperature | | | 180~220 | °C |
| Processing temperature | | | 190~230 | °C |
| Processing temperature | | | 180~230°C | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.