ABS TAIRILAC® AF3500 FCFC TAIWAN
1584
- Properties:High mobilityHigh impact resistanceHigh liquidityHigh impact resistance
- Usages:Computer accessoriesShellHousehold appliancesToy
- Certificates:ULMSDSTDSProcessingMSDSULRoHSSVHCEnvironmental
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.04 | g/cm³ | |
| 23°C | ISO1183 | 1.04 | g/cm³ | |
| 200°C/5.0kg | ASTMD1238 | 5.0 | g/10min | |
| 220°C/10.0kg | ASTMD1238 | 50 | g/10min | |
| 200°C/5.0kg | ISO1133 | 5.0 | g/10min | |
| 220°C/10.0kg | ISO1133 | 50 | g/10min | |
| Shrinkage rate | MD | 内部方法 | 0.40to0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | 屈服,23°C | ISO527-2 | 39.0 | Mpa |
| Bending modulus | 23°C | ASTMD790 | 2160 | Mpa |
| 23°C | ISO178 | 2160 | Mpa | |
| bending strength | 23°C | ASTMD790 | 67.0 | Mpa |
| Bending stress | 23°C | ISO178 | 67.0 | Mpa |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ISO180 | 290 | J/m |
| 23°C,6.35mm | ASTMD256 | 290 | J/m | |
| Tensile strength | 23°C | ASTMD638 | 39.2 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,12.7mm | ISO75-2/A | 84.0 | °C |
| 1.8MPa,Annealed | ASTMD648 | 94.0 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 94.0 | °C | |
| Vicat softening temperature | ASTMD15253 | 99.0 | °C | |
| ISO306/A | 99.0 | °C | ||
| Hot deformation temperature | 1.8MPa,未退火,12.7mm | ASTMD648 | 84.0 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.