Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Melt mass flow rate | 337°C/6.6kg | ASTMD1238 | 13 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| FlexuralStrength5 | Yield,50.0mmSpan | ASTMD790 | 207 | Mpa |
| Flexural Strength4 | Break,100mmSpan | ASTMD790 | 207 | Mpa |
| Bending modulus | 100mmSpan4 | ASTMD790 | 6890 | Mpa |
| Bending modulus | 50.0mm跨距5 | ASTMD790 | 6890 | Mpa |
| Elongation rate 3 | 屈服 | ASTMD638 | 3.0 | % |
| Tensile modulus 2 | | ASTMD638 | 6890 | Mpa |
| Tensile strength 3 | 屈服 | ASTMD638 | 138 | Mpa |
| Tensile strength 3 | 断裂 | ASTMD638 | 138 | Mpa |
| Elongation rate 4 | 断裂 | ASTMD638 | 3.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 211 | °C |
| Hot deformation temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 214 | °C |
| Hot deformation temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 206 | °C |
| Hot deformation temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 209 | °C |
| Vicat softening temperature | | ASTMD15256 | 210 | °C |
| RTIElec | | UL746 | 105 | °C |
| Evolution Calendar intelligent importer | | UL746 | 105 | °C |
| RTIStr | | UL746 | 105 | °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 3.6E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.2E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot wire ignition | HWI | UL746 | PLC1 | |
| High arc combustion index | HAI | UL746 | PLC3 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 | |
| Arc resistance 7 | | ASTMD495 | PLC6 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 14.9 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| FlameRating | 0.41mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.