PA6 DP BKV 60 H2.0 EF 900116 LANXESS GERMANY
Durethan®
--
Filler: Glass fiber reinf、60% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/LANXESS GERMANY/DP BKV 60 H2.0 EF 900116
Shrinkage rate
TD:280°C,2.00mm2
ISO2577
%
0
Shrinkage rate
TD:120°C,4小时,2.00mm3
ISO2577
%
0
Shrinkage rate
MD:280°C,2.00mm2
ISO2577
%
0
Shrinkage rate
MD:120°C,4小时,2.00mm3
ISO2577
%
0
Water absorption rate
饱和,23°C
ISO62
%
3
Water absorption rate
平衡,23°C,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA6/LANXESS GERMANY/DP BKV 60 H2.0 EF 900116
Tensile modulus
23°C
ISO527-2/1
Mpa
1
Tensile strain
断裂,23°C
ISO527-2/5
%
2
Tensile stress
断裂,23°C
ISO527-2/5
Mpa
2
Bending modulus 4
23°C
ISO178/A
Mpa
2
Bending strain 5
23°C
ISO178/A
%
3
Bending stress
3.5%Strain,23°C
ISO178/A
Mpa
-
Bending stress
23°C4
ISO178/A
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
PA6/LANXESS GERMANY/DP BKV 60 H2.0 EF 900116
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Hot deformation temperature
8.0MPa,未退火
ISO75-2/C
°C
1
Melting temperature 5
ISO11357-3
°C
2
Linear coefficient of thermal expansion
MD：23到55°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：23to55°C
ISO11359-2
cm/cm/°C
8
Impact performance
Test Condition
Test Method
Unit
PA6/LANXESS GERMANY/DP BKV 60 H2.0 EF 900116
Multi axis Instrumented Peak Impact Force
23°C
ISO6603-2
N
1
Multi axis Instrumented Peak Impact Force
-30°C
ISO6603-2
N
1
Multi axis Instrumented Impact Energy
-30°C
ISO6603-2
J
3
Multi axis Instrumented Impact Energy
23°C
ISO6603-2
J
4
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
9
Unscented Izod impact strength
-30°C
ISO180/1U
kJ/m²
9
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
9