Melt mass flow rate

300°C/1.2kg

ASTMD1238

g/10min

1

Shrinkage rate

MD：3.20mm

内部方法

%

0

Specific volume

ASTMD792

cm³/g

0

Water absorption rate

24hr

ASTMD570

%

0

Water absorption rate

平衡,23°C

ASTMD570

%

0

Water absorption rate

平衡,100°C

ASTMD570

%

0

Tensile strength 1

屈服

ASTMD638

Mpa

6

Tensile strength 1

断裂

ASTMD638

Mpa

6

Elongation rate 2

屈服

ASTMD638

%

7

Elongation rate 2

断裂

ASTMD638

%

1

Taber abraser

1000Cycles,1000g,CS-17转轮

ASTMD1044

mg

1

Bending modulus 3

50.0mm跨距

ASTMD790

Mpa

2

Bending strength 4

屈服,50.0mm跨距

ASTMD790

Mpa

9

RTI

UL746

°C

8

RTIElec

UL746

°C

8

Evolution Calendar intelligent importer

UL746

°C

8

specific heat

ASTMC351

J/kg/°C

1

thermal conductivity

ASTMC177

W/m/K

0

Hot deformation temperature

0.45MPa,未退火,6.40mm

ASTMD648

°C

1

Hot deformation temperature

1.8MPa,未退火,6.40mm

ASTMD648

°C

1

Vicat softening temperature

ASTMD152512

°C

1

Linear coefficient of thermal expansion

MD：-40到95°C

ASTME831

cm/cm/°C

6

Dielectric strength

3.20mm,inAir

ASTMD149

KV/mm

1

Volume resistivity

ASTMD257

ohms·cm

>

23°C

ASTMD256

J/m

6

23°C

ASTMD4812

J/m

3

23°C8

ISO180/1A

kJ/m²

6

-30°C7

ISO180/1A

kJ/m²

1

Impact strength of simply supported beam gap 5

23°C

ISO179/1eA

kJ/m²

6

Impact strength of simply supported beam gap 5

-30°C

ISO179/1eA

kJ/m²

1

Tensile impact strength 11

ASTMD1822

kJ/m²

5

Falling hammer impact

23°C

ASTMD3029

J

1

Hot filament ignition temperature

0.750mm13

IEC60695-2-13

°C

8

Hot filament ignition temperature

1.50mm

IEC60695-2-13

°C

8

Burning wire flammability index

0.750mm

IEC60695-2-12

°C

7

Burning wire flammability index

1.50mm

IEC60695-2-12

°C

8