Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM TF-10LV TAIWAN POLYPLASTICS
DURACON®
Electrical applications、Automotive Applications
High rigidity、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/TAIWAN POLYPLASTICS/TF-10LV
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
190°C/2.16kg
ISO1133
cm3/10min
9
Melt mass flow rate
190°C/2.16kg
ISO1133
g/10min
1
Shrinkage rate
TD:2.00mm
ISO294-4
%
1
Shrinkage rate
MD:2.00mm
ISO294-4
%
1
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/TAIWAN POLYPLASTICS/TF-10LV
Nominal tensile fracture strain
ISO527-2
%
5
Tensile modulus
ISO527-2
Mpa
1
Tensile stress
ISO527-2
Mpa
4
Wear factor
0.49MPa,0.30m/sec4
JISK7218
10^-8mm³/N·m
<
Wear factor
0.49MPa,0.30m/sec5
JISK7218
10^-8mm³/N·m
1
Wear factor
0.060MPa,0.15m/sec6
JISK7218
10^-8mm³/N·m
6
Wear factor
0.060MPa,0.15m/sec7
JISK7218
10^-8mm³/N·m
7
Bending modulus
ISO178
Mpa
1
Bending stress
ISO178
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
POM/TAIWAN POLYPLASTICS/TF-10LV
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
8
Linear coefficient of thermal expansion
MD：23到55°C
内部方法
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：23to55°C
内部方法
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
POM/TAIWAN POLYPLASTICS/TF-10LV
Surface resistivity
IEC60093
ohms
7
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
POM/TAIWAN POLYPLASTICS/TF-10LV
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1