Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML7672-739L SABIC INNOVATIVE NANSHA
LEXAN™
Electronic and electrical、Automotive components、Lighting fixtures
High temperature resistan、Flame retardant、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML7672-739L
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
5
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
4
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML7672-739L
--
ISO527-2/1
Mpa
5
--1
ASTMD638
Mpa
5
--5
ISO178
Mpa
5
50.0mm span 4
ASTMD790
Mpa
4
--6
ISO178
Mpa
1
crack
ISO527-2/5
Mpa
5
crack
ISO527-2/5
%
1
Fracture 2
ASTMD638
Mpa
5
Fracture 3
ASTMD638
%
5
yield
ISO527-2/5
%
0
yield
ISO527-2/5
Mpa
1
Yield, 50.0mm span 7
ASTMD790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML7672-739L
--
ASTM D152512, ISO 306/B50, ISO 306/B120
°C
1
--
ISO306/B120
°C
1
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
1
1.8MPa, unannealed, 64.0mm span of 10
ISO75-2/Af
°C
1
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831,ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831,ISO11359-2
cm/cm/°C
6
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/ML7672-739L
23°C
ASTMD256
J/m
2
23°C9
ISO180/1A
kJ/m²
1
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
2