MeltViscosity3

260°C

ISO11443-A

Pa·s

2

Density/specific gravity

23°C

ISO1183

g/cm³

1

Melt volume flow rate

260°C/5.0kg

ISO1133

cm3/10min

1

Shrinkage rate 2

TD:260°C,3.00mm

ISO2577

%

0

Shrinkage rate 2

MD:260°C,3.00mm

ISO2577

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

Tensile modulus

23°C

ISO527-2/1

Mpa

2

Tensile strain

断裂,23°C

ISO527-2/50

%

>

Tensile strain

屈服,23°C

ISO527-2/50

%

4

Tensile stress

屈服,23°C

ISO527-2/50

Mpa

5

Tensile stress

断裂,23°C

ISO527-2/50

Mpa

5

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

1

Vicat softening temperature

--

ISO306/B50

°C

1

Vicat softening temperature

--

ISO306/B120

°C

1

Linear coefficient of thermal expansion

MD：23到55°C

ISO11359-2

cm/cm/°C

7

Linear coefficient of thermal expansion

TD：23to55°C

ISO11359-2

cm/cm/°C

8

Surface resistivity

IEC60093

ohms

1

Dielectric strength

23°C,1.00mm

IEC60243-1

KV/mm

3

Leakage Trace Index

解决方案A

IEC60112

V

2

Volume resistivity

23°C

IEC60093

ohms·cm

1

Impact strength of cantilever beam gap

-30°C

ISO180/A

kJ/m²

3

Impact strength of cantilever beam gap

23°C

ISO180/A

kJ/m²

4