Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73G30HSL BK416 DUPONT JAPAN
Zytel®
Electronic and electrical、Automotive Applications
Thermal stability、30% filler by weight、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/DUPONT JAPAN/73G30HSL BK416
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
1
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
6
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA6/DUPONT JAPAN/73G30HSL BK416
TensileCreepModule
1hr
ISO899-1
Mpa
-
Tensile modulus
ISO527-2
Mpa
9
Tensile creep modulus
1000hr
ISO899-1
Mpa
-
Tensile strain
断裂
ISO527-2
%
3
Tensile stress
断裂
ISO527-2
Mpa
1
Bending modulus 2
ISO178
Mpa
8
Bending stress 2
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA6/DUPONT JAPAN/73G30HSL BK416
Glass transition temperature 3
ISO11357-2
°C
6
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature 5
ISO11357-3
°C
2
Vicat softening temperature
ISO306/B50
°C
2
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
7
Impact performance
Test Condition
Test Method
Unit
PA6/DUPONT JAPAN/73G30HSL BK416
Multi axis Instrumented Impact Energy
23°C
ISO6603-2
J
3
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
1
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
8
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
1
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
8
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
1
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
hardness
Test Condition
Test Method
Unit
PA6/DUPONT JAPAN/73G30HSL BK416
Ball pressure hardness
H961/30
ISO2039-1
Mpa
2
flammability
Test Condition
Test Method
Unit
PA6/DUPONT JAPAN/73G30HSL BK416
Extreme Oxygen Index 5
ISO4589-2
%
2
Burning rate 4
1.00mm
ISO3795
mm/min
5
atomization
F-value(refraction)
ISO6452
%
9
atomization
G-value(condensate)
ISO6452
g
1
Supplementary Information
Test Condition
Test Method
Unit
PA6/DUPONT JAPAN/73G30HSL BK416
EmissionofOrganicCompounds
VDA277
µgC/g
8