Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HPS1R-1124 SABIC INNOVATIVE US
LEXAN™
medicine、medical care
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/HPS1R-1124
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
2
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
2
Shrinkage rate
MD：3.20mm
内部方法
%
0
Specific volume
ASTMD792
cm³/g
0
Water absorption rate
24hr
ASTMD570
%
0
Water absorption rate
平衡,23°C
ASTMD570
%
0
Water absorption rate
平衡,100°C
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/HPS1R-1124
Tensile strength 3
屈服
ASTMD638
Mpa
6
Tensile strength 3
断裂
ASTMD638
Mpa
6
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus 2
ASTMD638
Mpa
2
Tensile strain
断裂
ISO527-2/50
%
7
Tensile strain
屈服
ISO527-2/50
%
6
Tensile stress
屈服
ISO527-2/50
Mpa
6
Tensile stress
断裂
ISO527-2/50
Mpa
5
Elongation rate 3
屈服
ASTMD638
%
6
Elongation rate 4
断裂
ASTMD638
%
1
Taber abraser
1000Cycles,1000g,CS-17转轮
ASTMD1044
mg
1
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus 5
ISO178
Mpa
2
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
9
Bending strength 5,6
ISO178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/HPS1R-1124
specific heat
ASTMC351
J/kg/°C
1
thermal conductivity
ASTMC177
W/m/K
0
thermal conductivity
ISO8302
W/m/K
0
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature 10
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
1
Hot deformation temperature 10
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到95°C
ASTME831
cm/cm/°C
6
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
7
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/HPS1R-1124
Surface resistivity
IEC60093
ohms
>
Dielectric strength
3.20mm,inAir
ASTMD149
KV/mm
1
Dielectric strength
3.20mm,在油中
IEC60243-1
KV/mm
1
Volume resistivity
ASTMD257
ohms·cm
>
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/HPS1R-1124
Impact strength of simply supported beam gap 7
23°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam gap 7
-30°C
ISO179/1eA
kJ/m²
1
Tensile impact strength 9
ASTMD1822
kJ/m²
3
Falling hammer impact
23°C
ASTMD3029
J
1
Suspended wall beam gap impact strength 8
23°C
ISO180/1A
kJ/m²
1
Suspended wall beam gap impact strength 8
-30°C
ISO180/1A
kJ/m²
1
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
5
hardness
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/HPS1R-1124
Ball pressure hardness
H358/30
ISO2039-1
Mpa
9
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/HPS1R-1124
Extreme Oxygen Index
ISO4589-2
%
2
optical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE US/HPS1R-1124
transmissivity
2540µm
ASTMD1003
%
8
Haze
2540µm
ASTMD1003
%
1