Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP J705UG PRIME POLYMER JAPAN
PRIME POLYPRO
--
High rigidity、Antistatic、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/J705UG
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
9
physical property
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/J705UG
Melt index
230℃,2.16kg
ISO 1133
g/10min
9
Melt mass flow rate
230°C/2.16kg
ISO1133
g/10min
9
Mechanical performance
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/J705UG
Fracture tensile strain
ISO 527-2
%
5
elongation at break
ASTM D638/ISO 527
%
5
Charpy Notched Impact Strength
-20℃
ISO 179
kJ/m²
4
Charpy Notched Impact Strength
23℃
ISO 179
kJ/m²
1
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Tensile modulus
ISO 527-2
Mpa
1
Tensile modulus
ISO527-2
Mpa
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
2
Tensile strain
断裂
ISO527-2
%
5
Tensile stress
屈服
ISO527-2
Mpa
2
Yield tensile stress
ISO 527-2
Mpa
2
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Thermal performance
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/J705UG
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Hot deformation temperature
0.45MPa,未退火
ISO 75-2/B
°C
1
Impact performance
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/J705UG
Impact strength of simply supported beam without notch
-20°C
ISO179
kJ/m²
4
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
1