PBT/PET PCR GF 30 BK A SCHULMAN USA
SCHULADUR®
--
Filler: Glass fiber reinf、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/PET/A SCHULMAN USA/PCR GF 30 BK
Melt volume flow rate
260°C/2.16kg
ISO1133
cm3/10min
2
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/PET/A SCHULMAN USA/PCR GF 30 BK
Tensile modulus
ISO527-2/1A/1
Mpa
1
Tensile strain
断裂
ISO527-2/1A/5
%
2
Tensile stress
断裂
ISO527-2/1A/5
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/PET/A SCHULMAN USA/PCR GF 30 BK
Hot deformation temperature
0.45MPa,未退火
ISO75-2/Bf
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/Af
°C
2
Vicat softening temperature
--
ISO306/A50
°C
2
Vicat softening temperature
--
ISO306/B50
°C
2
Electrical performance
Test Condition
Test Method
Unit
PBT/PET/A SCHULMAN USA/PCR GF 30 BK
Surface resistivity
IEC60093
ohms
>
Leakage Trace Index
IEC60112
V
3
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PBT/PET/A SCHULMAN USA/PCR GF 30 BK
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
5
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
5
hardness
Test Condition
Test Method
Unit
PBT/PET/A SCHULMAN USA/PCR GF 30 BK
Ball pressure hardness
H358/30
ISO2039-1
Mpa
2
flammability
Test Condition
Test Method
Unit
PBT/PET/A SCHULMAN USA/PCR GF 30 BK
Extreme Oxygen Index
ISO4589-2
%
1
Burning rate
ISO3795
mm/min
2
Hot filament ignition temperature
1.5mm
IEC60695-2-13
°C
7
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
8
Burning wire flammability index
1.5mm
IEC60695-2-12
°C
7
Burning wire flammability index
3.0mm
IEC60695-2-12
°C
8