Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS TR-557I LG CHEM KOREA
--
Automotive components
wear resistant、high strength、High impact resistance、High temperature resistan、 High impact
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/LG CHEM KOREA/TR-557I
Melt index
200°C/5kg
ASTM D624
g/10min
2
Shrinkage rate
ASTM D-955
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/LG CHEM KOREA/TR-557I
Stretching rate (resistance point)
50mm/min
ASTM D-638
%
≥
Stretching rate (breaking point)
50mm/min
ASTM D-638
%
5
Bending modulus
15mm/min
ASTM D-790
kg/cm2(MPa)
2
bending strength
15mm/min
ASTM D-790
kg/cm2(MPa)
6
Tension measurement
1mm/min
ASTM D-638
kg/cm2(MPa)
1
Tensile strength
50mm/min
ASTM D-638
kg/cm2(MPa)
4
IZOD impact strength
1/4",23°C
ASTM D-256
kg.cm/cm(J/m)
1
Thermal performance
Test Condition
Test Method
Unit
ABS/LG CHEM KOREA/TR-557I
Combustibility
1/8"
UL-94
CLASS
H
Combustibility
1/8"
IEC707
mm/min
-
Hot deformation temperature
4.6kg/cm21/4"annealed(unannealed)
ASTM D-648
°C
9
Hot deformation temperature
1.86kgf/cm21/4
ASTM D-648
°C
8
Microcard softening point
1kg/120℃/h(5kg/50℃/h)
ASTM D-1525
°C
9