Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 900P DUPONT JAPAN
Delrin®
Thin walled products、Fiber grade
wear resistant、High rigidity、high strength、enhance、High impact resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/DUPONT JAPAN/900P
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
190°C/2.16kg
ISO1133
cm3/10min
2
Melt mass flow rate
ISO1133
g/10min
2
Shrinkage rate
TD
ISO294-4
%
1
Shrinkage rate
MD
ISO294-4
%
1
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
1
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/DUPONT JAPAN/900P
TensileCreepModule
1hr
ISO899-1
Mpa
2
Nominal tensile fracture strain
ISO527-2
%
2
Tensile modulus
ISO527-2
Mpa
3
Tensile creep modulus
1000hr
ISO899-1
Mpa
1
Tensile strain
屈服
ISO527-2
%
1
Tensile stress
屈服
ISO527-2
Mpa
7
Bending modulus
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
POM/DUPONT JAPAN/900P
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
9
Melting temperature 2
ISO11357-3
°C
1
Vicat softening temperature
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD：23到55°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
POM/DUPONT JAPAN/900P
Hot-wireIgnition
0.750mm
UL746
sec
8
Surface resistivity
IEC60093
ohms
>
Leakage Trace Index
IEC60112
V
6
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
POM/DUPONT JAPAN/900P
Charpy Notched Impact Strength
-30°C
ISO179/1eA
kJ/m²
7
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
8
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
2
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
2
Impact strength of cantilever beam gap
-40°C
ISO180/1A
kJ/m²
8
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
7
flammability
Test Condition
Test Method
Unit
POM/DUPONT JAPAN/900P
Extreme Oxygen Index
ISO4589-2
%
2
Burning rate 3
1.00mm
ISO3795
mm/min
2
atomization
F-value(refraction)
ISO6452
%
9
atomization
G-value(condensate)
ISO6452
g
2
Supplementary Information
Test Condition
Test Method
Unit
POM/DUPONT JAPAN/900P
Emission
VDA275
mg/kg
<
EmissionofOrganicCompounds
VDA277
µgC/g
4