Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO/PA GTX9400W-1710 SABIC INNOVATIVE THAILAND
NORYL GTX™
Electrical applications、Industrial machinery
High mobility、dimensional stability 、High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/GTX9400W-1710 |
|---|---|---|---|
| Vicat Softening Temperature | ASTM D1525 | 212 °C | |
| Heat Deflection Temperature | 1.82MPa,6.4mm | ASTM D648 | 170 °C |
| Vicat Softening Temperature | ISO 306 | 203 °C | |
| Heat Deflection Temperature | 1.84MPa,3.2mm | ASTM D648 | 84 °C |
| Melting temperature | 270-295 °C | ||
| Heat Deflection Temperature | 0.45MPa,3.2mm | ASTM D648 | 191 °C |
| 0.45MPa,6.4mm | 203 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/GTX9400W-1710 |
|---|---|---|---|
| Modeling Shrinkage | flow,3.2mm | GE Method | 1.2-1.4 % |
| Melt index | ASTM D1238 | 97 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/GTX9400W-1710 |
|---|---|---|---|
| Tensile Stress | 50mm/min | ISO 527 | 69 Mpa |
| Izod Impact Strength | 无缺口，23℃ | ASTM D4812 | 849 J/m |
| 缺口，23℃ | ASTM D256 | 256 J/m | |
| 缺口，-30℃ | 112 J/m | ||
| Flexural Modulus | ASTM D790 | 2360 Mpa | |
| Tensile Modulus | 50mm/min | ASTM D638 | 1960 Mpa |
| Tensile Stress | 断裂 | 62 Mpa | |
| 屈服 | 65 Mpa | ||
| Flexural Stress | ASTM D790 | 101 Mpa | |
| Izod Impact Strength | 无缺口，-30℃ | ASTM D4812 | 769 J/m |
| Flexural Modulus | 2mm/min | ISO 178 | 2710 Mpa |
| Other | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/GTX9400W-1710 |
|---|---|---|---|
| Drying Time | 3-4 h | ||
| Drying Temperature | 95-105 °C |