POM/PTFE KAL-4022 BK SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive Applications
heat-resisting、high strength、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/PTFE/SABIC INNOVATIVE US/KAL-4022 BK
Shrinkage rate
MD：--2
内部方法
%
1
Shrinkage rate
MD：24hr
ASTMD955
%
2
Shrinkage rate
TD：24hr
ASTMD955
%
2
Mechanical performance
Test Condition
Test Method
Unit
POM/PTFE/SABIC INNOVATIVE US/KAL-4022 BK
Tensile modulus
ISO527-2/1
Mpa
3
Tensile modulus 3
ASTMD638
Mpa
3
Tensile strength 4
Break
ASTMD638
Mpa
5
Tensile strain
屈服
ISO527-2/5
%
6
Tensile strain
断裂
ISO527-2/5
%
7
Tensile stress
断裂
ISO527-2/5
Mpa
5
Tensile stress
屈服
ISO527-2/5
Mpa
5
Wear factor
Ring
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
0
Wear factor
Washer
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
8
Elongation rate 4
屈服
ASTMD638
%
6
Elongation rate 4
断裂
ASTMD638
%
7
Bending modulus 5
50.0mmSpan
ASTMD790
Mpa
3
Bending modulus 6
ISO178
Mpa
3
Bending stress
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
POM/PTFE/SABIC INNOVATIVE US/KAL-4022 BK
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 8
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
8
Impact performance
Test Condition
Test Method
Unit
POM/PTFE/SABIC INNOVATIVE US/KAL-4022 BK
NotchedIzodImpactStrength7
23°C
ISO180/1A
kJ/m²
5
UnnotchedIzodImpactStrength7
23°C
ISO180/1U
kJ/m²
3