Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A RV250AF 375 BK-PA1000B RADICI SUZHOU
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/RADICI SUZHOU/A RV250AF 375 BK-PA1000B
Shrinkage rate
垂直280℃ 60MPa模具温度:80℃
ISO 294
%
I
Shrinkage rate
流动280℃60MPa模具温度80℃
ISO 294
%
I
Moisture absorption rate
23℃ 50RH 2.00mm
ISO 62
%
I
Water absorption rate
23℃ 2.00mm在水里
ISO 62
%
I
Mechanical performance
Test Condition
Test Method
Unit
PA66/RADICI SUZHOU/A RV250AF 375 BK-PA1000B
Impact of simply supported beam gap
“-”30℃1eA型
ISO 179
kJ/m²
I
Impact of simply supported beam gap
23°C1eA型
ISO 179
kJ/m²
I
Simple supported beam without notch impact
-30。0
ISO 179
kJ/m²
I
Simple supported beam without notch impact
23℃
ISO 179
kJ/m²
I
Tensile modulus
1.0mm/min
ISO 527
Mpa
I
Tensile strength fracture
5mm/min
ISO 527
Mpa
I
Elongation at break
5mm/min
ISO 527
%
I
Bending modulus
2.0mm/min
ISO 178
Mpa
I
bending strength
2.0mm/min
ISO 178
Mpa
I
Thermal performance
Test Condition
Test Method
Unit
PA66/RADICI SUZHOU/A RV250AF 375 BK-PA1000B
Expansion coefficient flow
23~55℃
ISO 11359
m/m/k
I
Hot deformation temperature
1.8MPa
ISO 75
°C
I
Melting temperature
10℃/min
ISO 11357
°C
I
Vicat softening temperature
50℃/hr 50N
ISO 306
°C
I
Vertical coefficient of linear expansion
23~55℃
ISO 11359
m/m/k
I
Electrical performance
Test Condition
Test Method
Unit
PA66/RADICI SUZHOU/A RV250AF 375 BK-PA1000B
CTI solution A
IEC 60112
V
I
Surface resistance
500V
IEC 60093
Ω
I
Volume resistance
500V
IEC 60093
Ω.m
I