Melt volume flow rate

230℃，5 kg  230℃/5.0 kg

ISO 1133

cm3/10min

1

Water absorption rate

饱和，23℃  Saturation, 73°F

ISO 62

%

0

Water absorption rate

平衡，23℃，50% RH  Equilibrium, 73°F, 50% RH

ISO 62

%

0

Nominal tensile fracture strain

ISO 527-2

%

>

Tensile modulus

ISO 527-2

Mpa

1

tensile strength

屈服  屈服

ISO 527-2

Mpa

4

Tensile creep modulus

1 hr  1 hr

ISO 899-1

Mpa

5

Tensile creep modulus

1000 hr  1000 hr

ISO 899-1

Mpa

2

Tensile strain

屈服  屈服

ISO 527-2

%

1

Glass transition temperature

ISO 11357-2

°C

-

Hot deformation temperature

0.45 MPa，未退火  66 psi, Unannealed

ISO 75-2/B

°C

1

Hot deformation temperature

1.8 MPa，未退火  264 psi, Unannealed

ISO 75-2/A

°C

4

Melting temperature 3 3

ISO 11357-3

°C

1

Vicat softening temperature

B50  B50

ISO 306

°C

1

Linear coefficient of thermal expansion

MD  MD

ISO 11359-2

1/℃

0

Surface resistivity

IEC 60093

ohms

1

Dielectric strength

IEC 60243-1

KV/mm

2

Volume resistivity

IEC 60093

ohms·cm

2

Compared to the leakage trace index

IEC 60112

V

6

Extreme Oxygen Index

ISO 4589-2

%

4