Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 6300T JAPAN POLYPLASTIC
DURANEX®
Electrical applications、Electronic and electrical
Low friction coefficient、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/6300T
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/6300T
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
tensile strength
ISO 527-1/-2
Mpa
1
Tensile strain
断裂
ISO527-2
%
3
Tensile stress
ISO527-2
Mpa
1
Bending modulus
ISO178
Mpa
9
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
bending strength
ISO 178
Mpa
1
bending strength
ISO 178
Mpa
9
Bending stress
ISO178
Mpa
1
Charpy notch impact strength
ISO 179/1eA
KJ/m
4
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
3
Thermal performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/6300T
Hot deformation temperature
1.8Mpa
ISO 75-1/-2
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Linear coefficient of thermal expansion
MD：23到55°C
内部方法
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：23to55°C
内部方法
cm/cm/°C
7
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
3
Electrical performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/6300T
Surface resistivity
IEC 60093
Ω
1
Dielectric strength
3.00mm
IEC60243-1
KV/mm
1
Leakage Trace Index
IEC60112
V
2
Resistance to conductive traces
IEC 60112
CTI
2
Volume resistivity
IEC 60093
Ω.cm
6
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
6
Volume resistivity
IEC60093
ohms·cm
6