Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 357 BK1066 SABIC INNOVATIVE SHANGHAI
XENOY™
Lawn equipment、Electrical field、Electrical appliances、Electronic field、Electronic display、Engine hood parts、Industrial applications、Nursing supplies、Household goods、Architectural application、Petroleum Applications、Outdoor applications、Natural gas supplies、Liquid handling、Medical supplies、Garden equipment、Lighting fixtures、switch、Shell、Spool
Impact modification
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE SHANGHAI/357 BK1066
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
8
Melt mass flow rate
250°C/5.0kg
ASTMD1238
g/10min
9
Shrinkage rate
MD：--2
内部方法
%
0
Shrinkage rate
MD：--3
内部方法
%
1
Shrinkage rate
MD：3.20mm
内部方法
%
1
Shrinkage rate
TD：--2
内部方法
%
0
Shrinkage rate
TD：--3
内部方法
%
1
Specific volume
ASTMD792
cm³/g
0
Water absorption rate
24hr
ASTMD570
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE SHANGHAI/357 BK1066
FlexuralStrength6
Break,50.0mmSpan
ASTMD790
Mpa
7
Tensile strength 6
屈服
ASTMD638
Mpa
4
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus 4
ASTMD638
Mpa
2
Tensile strength 5
Break
ASTMD638
Mpa
4
Tensile strain
断裂
ISO527-2/50
%
3
Tensile strain
屈服
ISO527-2/50
%
5
Tensile strain 5
Break
ASTMD638
%
5
Tensile strain 5
Yield
ASTMD638
%
5
Tensile stress
断裂
ISO527-2/50
Mpa
4
Tensile stress
屈服
ISO527-2/50
Mpa
5
Bending modulus 7
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus 7
ISO178
Mpa
2
Bending strength 7
屈服,50.0mm跨距
ASTMD790
Mpa
7
Bending strength 7,8
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE SHANGHAI/357 BK1066
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
RTIStr
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature 12
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
8
Vicat softening temperature
ASTMD152513
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40to40°C
ASTME831
cm/cm/°C
9
Linear coefficient of thermal expansion
MD：60to138°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
8
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE SHANGHAI/357 BK1066
Dielectric strength
1.60mm,在油中
ASTMD149
KV/mm
2
Dielectric strength
3.20mm,inAir
ASTMD149
KV/mm
1
Dielectric strength
3.20mm,在油中
ASTMD149
KV/mm
1
Volume resistivity
ASTMD257
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE SHANGHAI/357 BK1066
CharpyNotchedImpactStrength9
23°C
ISO179/1eA
kJ/m²
4
Falling hammer impact
23°C
ASTMD3029
J
4
Falling hammer impact
23°C11
ASTMD3029
J
4
Suspended wall beam gap impact strength 10
-30°C
ISO180/1A
kJ/m²
1
Suspended wall beam gap impact strength 10
23°C
ISO180/1A
kJ/m²
4
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
3
flammability
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE SHANGHAI/357 BK1066
Extreme Oxygen Index
ASTMD2863
%
3
Hot filament ignition temperature
2.0mm
IEC60695-2-13
°C
7
Hot filament ignition temperature
3.0mm
IEC60695-2-13
°C
7
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
7
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
9