Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 1010 GY2E570 SABIC INNOVATIVE US
ULTEM™
Food service sector
High temperature resistan、transparent、enhance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1010 GY2E570 |
|---|---|---|---|
| RTI | UL 746 | 170 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 198 °C |
| Thermal Conductivity | ASTM C177 | 0.22 W/m/K | |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 207 °C |
| RTI Imp | UL 746 | 170 °C | |
| RTI Elec | UL 746 | 170 °C | |
| Coefficient of Linear Thermal Expansion (Flow) | -20 到 150°C | ASTM E831 | 5.6E-5 cm/cm/°C |
| Vicat Softening Temperature | ASTM D15255 | 218 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/1010 GY2E570 |
|---|---|---|---|
| Rockwell Hardness | M 级 | ASTM D785 | 109 |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/1010 GY2E570 |
|---|---|---|---|
| Middle Temperature | 340 到 400 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Suggested Shot Size | 40 到 60 % | ||
| Drying Temperature | 150 °C | ||
| Mold Temperature | 135 到 165 °C | ||
| Vent Depth | 0.025 到 0.076 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 350 到 400 °C | ||
| Rear Temperature | 330 到 400 °C | ||
| Nozzle Temperature | 345 到 400 °C | ||
| Front Temperature | 345 到 400 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/1010 GY2E570 |
|---|---|---|---|
| Melt Mass-Flow Rate | 337°C/6.6 kg | ASTM D1238 | 18 g/10 min |
| Moisture Absorption | 平衡, 23°C | ASTM D570 | 1.3 % |
| 24 hr | ASTM D570 | 0.25 % | |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1010 GY2E570 |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | 3580 Mpa | |
| Tensile Strength | 屈服 | ASTM D638 | 110 Mpa |
| Flexural Modulus | 100 mm 跨距 | ASTM D790 | 3510 Mpa |
| Tensile Elongation | 屈服 | ASTM D638 | 7.0 % |
| 断裂 | ASTM D638 | 60 % | |
| Flexural Strength | 屈服, 100 mm 跨距 | ASTM D790 | 165 Mpa |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1010 GY2E570 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 1300 J/m |
| Gardner Impact | 23°C | ASTM D3029 | 33.0 J |
| Reverse Notch Izod Impact | 3.20 mm | ASTM D256 | 1200 J/m |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/1010 GY2E570 |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 |
| 3.0 mm | UL 94 | 5VA | |
| Oxygen Index | ASTM D2863 | 44 % |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1010 GY2E570 |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | 1.0E+17 ohms·cm | |
| Hot-wire Ignition | UL 746 | PLC 1 | |
| Dielectric Constant | 1 kHz | ASTM D150 | 3.15 |
| Dissipation Factor? | 1 kHz | ASTM D150 | 1.3E-3 |
| Arc Resistance | ASTM D495 | PLC 5 | |
| Dielectric Strength | 1.60 mm, in Air | ASTM D149 | 33 KV/mm |
| Comparative Tracking Index | UL 746 | PLC 4 | |
| High Amp Arc Ignition | UL 746 | PLC 3 | |
| Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 28 KV/mm |
| Dissipation Factor? | 2.45 GHz | ASTM D150 | 2.5E-3 |
| High Voltage Arc Tracking Rate | UL 746 | PLC 2 |