Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM/GF/PTFE KFL4016NC SABIC INNOVATIVE US
LNP™ LUBRICOMP™
household electrical appl、Lighting fixtures
High temperature resistan、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/GF/PTFE/SABIC INNOVATIVE US/KFL4016NC
Shrinkage rate
流动 : 24小时
ASTM D955
%
1
Shrinkage rate
横向流动 : 24小时
ASTM D955
%
1
Shrinkage rate
横向流量 : 24小时
ISO 294-4
%
1
Shrinkage rate
流量 : 24小时
ISO 294-4
%
1
Water absorption rate
24 hr, 50% RH
ASTM D570
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/GF/PTFE/SABIC INNOVATIVE US/KFL4016NC
Tensile strength
屈服
ASTM D638
Mpa
5
Tensile strength
屈服
ISO 527-2
Mpa
4
Tensile strength
断裂
ASTM D638
Mpa
5
Tensile strength
断裂
ISO 527-2
Mpa
4
Tensile modulus
-- 1
ASTM D638
Mpa
6
Tensile modulus
--
ISO 527-2/1
Mpa
5
Wear factor 2
ASTM D3702
10^-8 mm³/N·m
1
elongation
屈服
ASTM D638
%
3
elongation
屈服
ISO 527-2
%
2
elongation
断裂
ASTM D638
%
2
elongation
断裂
ISO 527-2
%
4
Bending modulus
--
ASTM D790
Mpa
5
Bending modulus
--
ISO 178
Mpa
6
bending strength
ASTM D790, ISO 178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
POM/GF/PTFE/SABIC INNOVATIVE US/KFL4016NC
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 3
ISO 75-2/Af
°C
1
Impact performance
Test Condition
Test Method
Unit
POM/GF/PTFE/SABIC INNOVATIVE US/KFL4016NC
Non notched cantilever beam impact
23°C
ASTM D4812
J/m
2
Non notched cantilever beam impact
23°C 3
ISO 180/1U
kJ/m²
1
Dart impact equipped with measuring instruments
23°C, Energy at Peak
ASTM D3763
J
9
Dart impact equipped with measuring instruments
--
ISO 6603-2
J
2