Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA LI-913 LG CHEM KOREA
--
Electrical field、Electrical appliances、Electronic field
High impact resistance、Weather resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ASA/LG CHEM KOREA/LI-913
Density/specific gravity
g/cm
1.07
A
Mold shrinkage rate
Flow
%
0.40-0.70
A
Mechanical performance
Test Condition
Test Method
Unit
ASA/LG CHEM KOREA/LI-913
Izod notch impact strength
23℃，3.18mm
J/m
395
A
Charpy impact strength
-30℃
KJ/m
42.2
I
Charpy impact strength
23℃
KJ/m
No Break
I
Charpy Notched Impact Strength
-30℃
KJ/m
3.90
I
Charpy Notched Impact Strength
23℃
KJ/m
50.2
I
Tensile fracture strain
%
28
I
Tensile modulus
MPa
1100
I
Tensile yield strength
MPa
39.3
A
Tensile yield strength
MPa
39.0
I
Tensile yield strain
%
5.0
I
Bending modulus
MPa
1960
A
bending strength
MPa
66.9
A
Thermal performance
Test Condition
Test Method
Unit
ASA/LG CHEM KOREA/LI-913
Hot deformation temperature
1.80MPa，未退火
℃
91.1
A
Vicat softening temperature
℃
103
A
Vicat softening temperature
50℃/h，B(50N)
℃
93.8
I
Linear coefficient of thermal expansion
Flow
cm/cm/℃
0.000094
I
Linear coefficient of thermal expansion
Transverse
cm/cm/℃
0.000094
I
Basic performance
Test Condition
Test Method
Unit
ASA/LG CHEM KOREA/LI-913
Melt index
220℃/10.0kg
g/10min
6.0
A
Melt index
220℃/10kg
cm
7.80
I
Water absorption rate
Soultion
%
0.40
I