Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1402SH XA1 ASAHI JAPAN
Leona™
Wire and cable applicatio、Wire sheath、Washer、Clip、Joint、Connector、parts、Application in the automo、Hose
Medium viscosity、Excellent articulation、Plasticity and demolding 、Used for rapid modeling c
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1402SH XA1
Shrinkage rate
干
旭化成方法
%
1
Shrinkage rate
MD
内部方法
%
1
Water absorption rate
平衡,23°C,50%RH
ISO62
%
-
Mechanical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1402SH XA1
Fracture elongation rate
干(湿)
ASTM D-638
%
5
Flexural strength
干(湿)
ASTM D-790
Mpa
1
Scratch resistance coefficient
干(湿)
ASTM D-790
GPa
2
Tensile strength
ASTMD638
Mpa
7
Tensile modulus
23°C
ISO527-2
Mpa
3
tensile strength
干(湿)
ASTM D-638
Mpa
7
Tensile strain
屈服,23°C
ISO527-2
%
4
Tensile strain
断裂,23°C
ISO527-2
%
-
Tensile stress
屈服,23°C
ISO527-2
Mpa
8
Rockwell hardness
干(湿)
ASTM D-785
M Scale
8
Rockwell hardness
干(湿)
ASTM D-785
R scale
1
elongation
断裂
ASTMD638
%
5
Taber abraser
1000Cycles
ASTMD1044
mg
-
Bending modulus
ASTMD790
Mpa
2
Bending modulus
23°C
ISO178
Mpa
2
bending strength
ASTMD790
Mpa
1
Bending stress
23°C
ISO178
Mpa
1
Cantilever beam notch impact strength
干(湿)
ASTM D-256
J/m
3
Thermal performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1402SH XA1
Hot deformation temperature
0.45MPa,未退火
ASTMD648
°C
2
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
6
Hot deformation temperature
0.46MPa,干
ASTM D-648
°C
2
Hot deformation temperature
1.82MPa,干
ASTM D-648
°C
7
Linear coefficient of thermal expansion
MD
ASTMD696
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1402SH XA1
Surface resistivity
IEC60093
ohms
1
Dielectric strength
IEC60243-1
KV/mm
2
Leakage Trace Index
3.00mm
IEC60112
V
5
Volume resistivity
23°C
IEC60093
ohms·cm
1
flammability
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1402SH XA1
Extreme Oxygen Index
ASTMD2863
%
2
Other performance
Test Condition
Test Method
Unit
PA66/ASAHI JAPAN/1402SH XA1
Oxygen index
干
ASTM D-2863
%
2