Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HPS6R-1125 SABIC INNOVATIVE CANADA
LEXAN™
medicine、medical care
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE CANADA/HPS6R-1125
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
6
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
7
Melt mass flow rate
300°C/5.0kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：--2
内部方法
%
0
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Water absorption rate
24hr
ASTMD570
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE CANADA/HPS6R-1125
FlexuralStrength5
Yield,50.0mmSpan
ASTMD790
Mpa
9
Tensile strength 4
屈服
ASTMD638
Mpa
6
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus 3
ASTMD638
Mpa
2
Tensile strength 4
Break
ASTMD638
Mpa
6
Tensile strain
断裂
ISO527-2/50
%
1
Tensile strain
屈服
ISO527-2/50
%
6
Tensile stress
断裂
ISO527-2/50
Mpa
7
Tensile stress
屈服
ISO527-2/50
Mpa
6
Elongation rate 4
屈服
ASTMD638
%
6
Elongation rate 4
断裂
ASTMD638
%
1
Bending modulus 5
50.0mmSpan
ASTMD790
Mpa
2
Bending modulus 6
ISO178
Mpa
2
Bending strength 6,7
ISO178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE CANADA/HPS6R-1125
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature 10
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
Vicat softening temperature
ASTMD152511
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
5
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
6
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
6
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE CANADA/HPS6R-1125
Impact strength of simply supported beam gap 8
-30°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
7
Suspended wall beam gap impact strength 9
-30°C
ISO180/1A
kJ/m²
1
Suspended wall beam gap impact strength 9
23°C
ISO180/1A
kJ/m²
7
Dart impact equipped with measuring instruments
23°C,EnergyatPeakLoad
ASTMD3763
J
6
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
6