Density/specific gravity

ASTMD792

g/cm³

1

Shrinkage rate

MD：3.20mm

内部方法

%

1

Shrinkage rate

TD：3.20mm

内部方法

%

1

Specific volume

ASTMD792

cm³/g

0

Water absorption rate

24hr

ASTMD570

%

0

Tensile strength 2

屈服

ASTMD638

Mpa

4

Elongation rate 2

断裂

ASTMD638

%

1

Bending modulus 4

50.0mm跨距

ASTMD790

Mpa

1

Bending strength 4

屈服,50.0mm跨距

ASTMD790

Mpa

6

RTIElec

UL746

°C

7

Evolution Calendar intelligent importer

UL746

°C

7

RTIStr

UL746

°C

7

Hot deformation temperature

0.45MPa,未退火,3.20mm

ASTMD648

°C

9

Hot deformation temperature

0.45MPa,未退火,6.40mm

ASTMD648

°C

9

Hot deformation temperature

1.8MPa,未退火,3.20mm

ASTMD648

°C

5

Hot deformation temperature

1.8MPa,未退火,6.40mm

ASTMD648

°C

6

Linear coefficient of thermal expansion

MD：-40to40°C

ASTME831

cm/cm/°C

9

Linear coefficient of thermal expansion

MD：60to138°C

ASTME831

cm/cm/°C

1

Linear coefficient of thermal expansion

TD：-40到40°C

ASTME831

cm/cm/°C

9

Dielectric strength

1.60mm,在油中

ASTMD149

KV/mm

2

Dielectric strength

3.20mm,inAir

ASTMD149

KV/mm

1

Dielectric strength

3.20mm,在油中

ASTMD149

KV/mm

1

Volume resistivity

ASTMD257

ohms·cm

5

Falling hammer impact

23°C4

ASTMD3029

J

5

Falling hammer impact

23°C

ASTMD3029

J

5

Impact strength of cantilever beam gap

23°C

ASTMD256

J/m

9

Impact strength of cantilever beam gap

23°C

ASTMD4812

J/m

1

Impact strength of cantilever beam gap

-30°C

ASTMD256

J/m

6