PBT 325FC-1001 SABIC INNOVATIVE SHANGHAI
VALOX™
Electrical appliances、Industrial applications、Construction field、Automotive External Parts、Outdoor applications
Easy to process
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/325FC-1001
Melt volume flow rate
250°C/2.16kg
ISO1133
cm3/10min
2
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
5
Shrinkage rate
MD
内部方法
%
2
Shrinkage rate
TD
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/325FC-1001
--
ISO527-2/1
Mpa
2
--2
ASTMD638
Mpa
2
crack
ISO527-2/50
Mpa
6
crack
ISO527-2/50
%
1
Fracture 4
ASTMD638
Mpa
6
Fracture 6
ASTMD638
%
1
yield
ISO527-2/50
%
1
yield
ISO527-2/50
Mpa
6
Surrender 3
ASTMD638
Mpa
6
Surrender 5
ASTMD638
%
7
Bending modulus 7
ISO178
Mpa
2
Bending stress 8
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/325FC-1001
--
ASTMD1525,ISO306/B50,ISO306/B12014
°C
1
--
ASTMD1525,ISO306/A501015
°C
2
0.45MPa, unannealed, 64.0mm span
ISO75-2/Bf
°C
1
1.8MPa, unannealed, 64.0mm span
ISO75-2/Af
°C
5
Filling analysis
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/325FC-1001
Melt viscosity
260°C,1500sec^-1
ISO11443
Pa·s
1
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/325FC-1001
0°C
ASTMD256
J/m
3
0°C10
ISO180/1A
kJ/m²
4
23°C
ASTMD256
J/m
3
23°C11
ISO180/1A
kJ/m²
4
-30°C
ASTMD256
J/m
3
-30°C12
ISO180/1U
kJ/m²
1
-30°C9
ISO180/1A
kJ/m²
4
Impact strength of simply supported beam without notch
-30°C
ISO179/2U
kJ/m²
8
hardness
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/325FC-1001
Ball pressure hardness
H358/30
ISO2039-1
Mpa
1