PC/PBT 5220U-1001 SABIC INNOVATIVE NANSHA
XENOY™
Electrical appliances、Electronic display、Automotive External Parts、Lighting applications
UV resistance、Antichemical、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/5220U-1001
Dissolved Volume Flow Rate (MVR)
250°C/5.0 kg
ASTM D1238, ISO 1133
cm3/10min
1
Melt flow rate
250°C/5.0 kg
ISO 1133
g/10 min
1
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
横向流动 2
内部方法
%
0
Specific volume
ASTM D792
cm³/g
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/5220U-1001
Tensile strength
屈服 5
ASTM D638
Mpa
5
Tensile strength
屈服
ISO 527-2/50
Mpa
5
Tensile strength
断裂 5
ASTM D638
Mpa
5
Tensile strength
断裂
ISO 527-2/50
Mpa
5
Tensile modulus
-- 3
ASTM D638
Mpa
2
Tensile modulus
-- 4
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 5
ASTM D638
%
4
elongation
屈服
ISO 527-2/50
%
4
elongation
断裂 5
ASTM D638
%
1
elongation
断裂
ISO 527-2/50
%
1
Bending modulus
50.0 mm 跨距 6
ASTM D790
Mpa
2
Bending modulus
-- 7
ISO 178
Mpa
2
Bending stress
-- 7, 8
ISO 178
Mpa
8
Bending stress
屈服, 50.0 mm 跨距 6
ASTM D790
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/5220U-1001
RTI
UL 746
°C
7
RTI Elec
UL 746
°C
7
RTI Imp
UL 746
°C
7
Vicat softening temperature
--
ASTM D152511
°C
1
Vicat softening temperature
--
ISO 306/B50
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831, ISO 11359-2
cm/cm/°C
9
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
9
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
9
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
8
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
9
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10
ISO 75-2/Af
°C
7
Impact performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/5220U-1001
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
6