Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-705 ZHENJIANG CHIMEI
POLYLAC®
Office supplies、Electrical field、Electronic field、Automotive sector、Plastic toy、Lighting fixtures
High mobility、High gloss
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
ABS/ZHENJIANG CHIMEI/PA-705
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
2
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
2
Mechanical performance
Test Condition
Test Method
Unit
ABS/ZHENJIANG CHIMEI/PA-705
IZOD notch impact strength
1/4"，23℃
ASTM D-256
kg-cm/cm(ft-lb/in)
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
Rockwell hardness
1/2"
ASTM D-785
R scale
1
elongation
ASTM D638/ISO 527
%
3
Flexural elasticity
1/4"，2.8mm/min
ASTM D-790
kg/cm2
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
5
bending strength
1/4"，2.8mm/min
ASTM D-790
kg/cm2(lb/in2)
6
Elongation rate
1/8"，6mm/min
ASTM D-638
%
2
Tensile strength
1/8"，6mm/min
ASTM D-638
kg/cm2(lb/in2)
4
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
2
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Thermal performance
Test Condition
Test Method
Unit
ABS/ZHENJIANG CHIMEI/PA-705
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
9
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
8
Hot deformation temperature
1/4"，50℃/hr
ASTM D-648
℃（℉）
9
softening point
1/8"，50℃/hr
ASTM D-1525
℃（℉）
1
vicat softening point
ASTM D1525/ISO R306
℃（℉）
1
Basic performance
Test Condition
Test Method
Unit
ABS/ZHENJIANG CHIMEI/PA-705
Melt index
200℃，5kg
ASTM D-1238
g/10min
2