Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1184G-A30 TORAY JAPAN
Toraycon®
Electrical components
High toughness、Flame retardant、Filler: Glass fiber reinf、15% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1184G-A30
Shrinkage rate
TD:3.00mm2
内部方法
%
1
Shrinkage rate
MD:3.00mm4
内部方法
%
0
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1184G-A30
Tensile modulus
23°C
ISO527-2
Mpa
6
Tensile strain
断裂,23°C
ISO527-2
%
2
Tensile stress
屈服,23°C
ISO527-2
Mpa
1
Bending modulus
23°C
ISO178
Mpa
6
Bending stress
23°C
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1184G-A30
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Linear coefficient of thermal expansion
MD：-30到100°C
ISO11359-2
cm/cm/°C
5
Electrical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1184G-A30
Dielectric strength
IEC60243-1
KV/mm
1
Arc resistance 7
IEC60950
sec
1
Volume resistivity
IEC60093
ohms·cm
5
Impact performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1184G-A30
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
3
Supplementary Information
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1184G-A30
BarFlowLength8
250°C,1.00mm
内部方法
mm
1