Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA612 158 NC010 DUPONT USA
Zytel®
Engineering accessories、Automotive Applications
Mineral reinforcement、Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Molding shrinkage rate
ASTM D955
%
1
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
1
physical property
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Shrinkage rate
TD
ISO294-4
%
1
Shrinkage rate
MD
ISO294-4
%
1
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
3
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
1
Stickiness number
96%H2SO4
ISO307
cm³/g
1
Mechanical performance
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Nominal tensile fracture strain
ISO527-2
%
3
elongation at break
ASTM D412/ISO 527
%
3
Tensile modulus
ASTM D412/ISO 527
kg/cm²(MPa)[Lb/in²]
2
Tensile modulus
ISO527-2
Mpa
2
tensile strength
ASTM D412/ISO 527
kg/cm²(MPa)[Lb/in²]
6
Tensile strain
屈服
ISO527-2
%
4
Tensile stress
屈服
ISO527-2
Mpa
6
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
N
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
5
Thermal performance
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Glass transition temperature 2
ISO11357-2
°C
6
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
6
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
6
Melting temperature 2
ISO11357-3
°C
2
Vicat softening temperature
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Dielectric strength
IEC60243-1
KV/mm
3
Volume resistivity
IEC60093
ohms·cm
>
film
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Tensile strain MD
Yield
ISO527-3
%
4
flammability
Test Condition
Test Method
Unit
PA612/DUPONT USA/158 NC010
Extreme Oxygen Index
ISO4589-2
%
2
Burning rate 3
1.00mm
ISO3795
mm/min
<