Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-747S TAIWAN CHIMEI
POLYLAC®
Home appliance components
High mobility
FDA
MSDS
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-747S
Density/specific gravity
--3
ASTMD792
g/cm³
1
Density/specific gravity
23°C
ISO1183
g/cm³
1
Melt volume flow rate
220°C/10.0kg
ISO1133
cm3/10min
2
Melt mass flow rate
200°C/5.0kg
ASTMD1238
g/10min
0
Shrinkage rate
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-747S
Tensile strength
屈服4
ASTMD638
Mpa
3
Tensile strength
屈服
ISO527-2/50
Mpa
4
Tensile strength
断裂
ISO527-2/50
Mpa
3
elongation
断裂4
ASTMD638
%
4
elongation
断裂
ISO527-2/50
%
2
Bending modulus
--5
ASTMD790
Mpa
2
Bending modulus
--6
ISO178
Mpa
1
bending strength
--5
ASTMD790
Mpa
6
bending strength
--6
ISO178
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-747S
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
8
Hot deformation temperature
1.8MPa,退火
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,退火
ISO75-2/A
°C
9
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
8
Vicat softening temperature
--
ASTMD15257
°C
1
Vicat softening temperature
--
ISO306/A50
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
9
Impact performance
Test Condition
Test Method
Unit
ABS/TAIWAN CHIMEI/PA-747S
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
2
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
3
Impact strength of cantilever beam gap
23°C,3.20mm
ASTMD256
J/m
4
Impact strength of cantilever beam gap
23°C,6.40mm
ASTMD256
J/m
3
Impact strength of cantilever beam gap
-30°C
ISO180/1A
kJ/m²
2
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
3