Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 2210EPR-1000 SABIC INNOVATIVE US
ULTEM™
Automotive components、Lighting fixtures
Thermal stability、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2210EPR-1000
Melt mass flow rate
337°C/6.6kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2210EPR-1000
Flexural Strength4
Break,100mmSpan
ASTMD790
Mpa
2
FlexuralStrength5
Yield,50.0mmSpan
ASTMD790
Mpa
2
Tensile strength 3
屈服
ASTMD638
Mpa
1
Tensile strength 3
断裂
ASTMD638
Mpa
1
Tensile modulus 2
ASTMD638
Mpa
6
Elongation rate 3
屈服
ASTMD638
%
3
Elongation rate 4
断裂
ASTMD638
%
3
Bending modulus
100mmSpan4
ASTMD790
Mpa
6
Bending modulus
50.0mm跨距5
ASTMD790
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2210EPR-1000
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
RTIStr
UL746
°C
1
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
2
Vicat softening temperature
ASTMD15256
°C
2
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/2210EPR-1000
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
1