Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM A25-03 MITSUBISHI ENGINEERING JAPAN
Iupital™
Electronic and Electrical、Automotive sector
High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/MITSUBISHI ENGINEERING JAPAN/A25-03
Melt volume flow rate
190°C/2.16kg
ISO1133
cm3/10min
1
Melt mass flow rate
190°C/2.16kg
ISO1133
g/10min
1
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/MITSUBISHI ENGINEERING JAPAN/A25-03
Nominal tensile fracture strain
ISO527-2
%
3
Tensile modulus
ISO527-2
Mpa
3
Tensile strain
屈服
ISO527-2
%
1
Tensile stress
屈服
ISO527-2
Mpa
6
Bending modulus
ISO178
Mpa
2
Bending stress
ISO178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
POM/MITSUBISHI ENGINEERING JAPAN/A25-03
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Melting temperature
ISO11357-3
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
POM/MITSUBISHI ENGINEERING JAPAN/A25-03
Surface resistivity
IEC60093
ohms
1
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
POM/MITSUBISHI ENGINEERING JAPAN/A25-03
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
2