Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS PA-749SK ZHENJIANG CHIMEI
POLYLAC®
Plate
high strength
SGS
UL
MSDS
RoHS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
ABS/ZHENJIANG CHIMEI/PA-749SK
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
0
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
9
Mechanical performance
Test Condition
Test Method
Unit
ABS/ZHENJIANG CHIMEI/PA-749SK
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
Rockwell hardness
ASTM D-785
R
1
elongation
ASTM D638/ISO 527
%
3
Flexural elasticity
ASTM D-790
104kg/cm2
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
6
bending strength
ASTM D-790
kg/cm2
6
Elongation rate
ASTM D-790
%
4
Tensile strength
ASTM D-638
kg/cm2
3
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
3
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
3
IZOD impact strength
1/8"
ASTM D-256
kg.cm/cm
4
IZOD impact strength
1/4"
ASTM D-256
kg.cm/cm
3
Thermal performance
Test Condition
Test Method
Unit
ABS/ZHENJIANG CHIMEI/PA-749SK
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
9
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
8
Hot deformation temperature
退火
ASTM D-648
℃(°F)
9
Hot deformation temperature
未退火
ASTM D-648
℃(°F)
8
vicat softening point
ASTM D-1525
℃(°F)
1
vicat softening point
ASTM D1525/ISO R306
℃（℉）
1
Basic performance
Test Condition
Test Method
Unit
ABS/ZHENJIANG CHIMEI/PA-749SK
Melt index
200℃ 5kg
ASTM D-1238
g/10min
0
Melt index
200℃ 10kg
ISO 1133
g/10min
5