Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO/PA GTX910 SABIC INNOVATIVE US
NORYL GTX™
Electrical applications、electrical equipment
High mobility、Chemical resistance、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/PA/SABIC INNOVATIVE US/GTX910
Shrinkage rate
流动 : 130°C, 1小时
ASTM D955
%
1
Shrinkage rate
流动 : 3.20 mm
内部方法
%
1
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
1
Water absorption rate
24 hr, 50% RH
ASTM D570
%
0
Water absorption rate
平衡, 50% RH
ASTM D570
%
1
Mechanical performance
Test Condition
Test Method
Unit
PPO/PA/SABIC INNOVATIVE US/GTX910
Tensile strength 2
屈服
ASTM D638
Mpa
5
Tensile strength 2
断裂
ASTM D638
Mpa
5
elongation
断裂
ASTM D638
%
6
Bending modulus
100 mm 跨距
ASTM D790
Mpa
2
bending strength
屈服, 100 mm 跨距
ASTM D790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PPO/PA/SABIC INNOVATIVE US/GTX910
RTI
UL 746
°C
5
RTI Elec
UL 746
°C
5
RTI Imp
UL 746
°C
5
Vicat softening temperature
ASTM D15254
°C
2
Linear coefficient of thermal expansion
流动 : -40 到 95°C
ASTM E831
cm/cm/°C
9
Linear coefficient of thermal expansion
流动 : 60 到 138°C
ASTM E831
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : -40 到 95°C
ASTM E831
cm/cm/°C
9
Linear coefficient of thermal expansion
横向 : 60 到 138°C
ASTM E831
cm/cm/°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Impact performance
Test Condition
Test Method
Unit
PPO/PA/SABIC INNOVATIVE US/GTX910
Dart impact equipped with measuring instruments
-30°C, Energy at Peak
ASTM D3763
J
3
Dart impact equipped with measuring instruments
23°C, Energy at Peak
ASTM D3763
J
5