Melt flow rate

260°C/5.0 kg

ASTM D1238

g/10 min

1

Shrinkage rate

流动 : 3.20 mm

内部方法

%

0

Shrinkage rate

横向流动 : 3.20 mm

内部方法

%

0

Water absorption rate

24 hr

ASTM D570

%

0

Water absorption rate

平衡, 23°C

ASTM D570

%

0

Tensile strength

屈服

ASTM D638

Mpa

5

elongation

断裂

ASTM D638

%

7

Bending modulus

50.0 mm 跨距

ASTM D790

Mpa

2

bending strength

屈服, 50.0 mm 跨距

ASTM D790

Mpa

8

RTI

UL 746

°C

6

RTI Elec

UL 746

°C

6

RTI Imp

UL 746

°C

6

thermal conductivity

ASTM C177

W/m/K

0

Vicat softening temperature

ASTM D15254

°C

1

Linear coefficient of thermal expansion

流动 : -20 到 150°C

ASTM E831

cm/cm/°C

7

Linear coefficient of thermal expansion

横向 : -20 到 150°C

ASTM E831

cm/cm/°C

7

Thermal deformation temperature under load

0.45 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Thermal deformation temperature under load

0.45 MPa, 未退火, 6.40 mm

ASTM D648

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 6.40 mm

ASTM D648

°C

1

Dart impact equipped with measuring instruments

-30°C, Total Energy

ASTM D3763

J

3

Dart impact equipped with measuring instruments

23°C, Total Energy

ASTM D3763

J

4