Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 8007F-600 JAPAN POLYPLASTIC
TOPAS®
LCD application、Optical applications
Dimensional stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-600
Melt flow index
260℃/2.16Kg
ISO1133
cm3/10min
3
Melt volume flow rate
190°C/2.16kg
ISO1133
cm3/10min
2
Melt volume flow rate
230°C/2.16kg
ISO1133
cm3/10min
1
Melt mass flow rate
190°C/2.16kg
ISO1133
g/10min
1
Melt mass flow rate
230°C/2.16kg
ISO1133
g/10min
1
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
(23°C,24hr)
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-600
elongation at break
23°C
ISO527-2
%
4
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
2
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
2
Tensile modulus
23°C
ISO527-2
Mpa
2
tensile strength
23°C
ISO527-2
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-600
Glass transition temperature
ISO11357-2
°C
7
Hot deformation temperature
0.45MPa未退火
ISO75-2/Bf
°C
7
Vicat softening temperature
ISO306/B50
°C
8
Vicat softening temperature
玻璃转化温度
ISO11357-2
°C
7
Electrical performance
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-600
Dissipation factor
相对漏电起痕指数
IEC60112
V
6
Dielectric constant
23°C
IEC60250
1kHz
2
Volume resistance
IEC60093
Ω.cm
1
film
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-600
Tensile modulus
MD:70µm,铸造薄膜
ISO527-3/1
Mpa
2
Tensile modulus
TD:70µm,铸造薄膜
ISO527-3/1
Mpa
1
Tensile stress
MD:断裂,70µm,铸造薄膜
ISO527-3/50
Mpa
5
Tensile stress
TD:断裂,70µm,铸造薄膜
ISO527-3/50
Mpa
5
elongation
MD:断裂,70µm,铸造薄膜
ISO527-3/50
%
3
elongation
TD:断裂,70µm,铸造薄膜
ISO527-3/50
%
3
Water vapor permeability
70µm,23°C,CastFilm,85%RH
ASTMF1249
g·mm/m²/atm/24hr
0
optical performance
Test Condition
Test Method
Unit
COC/JAPAN POLYPLASTIC/8007F-600
Transmittance 2000 μ m
ISO13468-2
%
9
Haze
70.0µm,铸造薄膜
ISO14782
%
>
Refractive index
ISO489
°C
1