Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 RF00AS-BK1A817 SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
Electronic and Electrical、Chemical equipment、mechanical、sporting goods
High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE NANSHA/RF00AS-BK1A817
Shrinkage rate (Across Flow)
xflow, 24
ASTM D 955
%
1
Longitudinal shrinkage rate (Flow)
flow, 24 h
ASTM D 955
%
0
Longitudinal shrinkage rate (Flow)
flow, 24 h
ISO 294
%
0
Moisture absorption rate
50% RH,
ASTM D 570
%
0
Moisture absorption rate
23°C / 50
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE NANSHA/RF00AS-BK1A817
Tensile modulus
50 mm/m
ASTM D638
Mpa
1
Tensile modulus
1 mm/min
ISO 527
Mpa
1
Tensile strength fracture (brk)
/
ASTM D638
Mpa
1
Tensile strength fracture (brk)
/
ISO 527
Mpa
1
Tensile elongation fracture (brk)
/
ASTM D638
%
2
Tensile elongation fracture (brk)
/
ISO 527
%
2
Bending modulus
/
ASTM D790
Mpa
1
Bending modulus
/
ISO 178
Mpa
1
bending strength
/
ASTM D790
Mpa
3
bending strength
/
ISO 178
Mpa
3
Impact performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE NANSHA/RF00AS-BK1A817
Multi axis impact
/
ISO 6603
J
3
Cantilever beam without notch (Izod Unnotched)
23℃ (73℉)80*10*4
ISO 180/1U
kJ/m²
6
Instrumented dart impact energy peak at 23 ℃ (73 ℉)
/
ASTM D3763
J
1
Thermal Properties
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE NANSHA/RF00AS-BK1A817
Coefficient of Linear Expansion (CLTE) Across Flow
-40°C to
ASTM E831
°C
4
Coefficient of Linear Expansion (CLTE) Across Flow
-40°C to
ISO 11359-2
°C
4
Coefficient of Linear Expansion (CLTE) Longitudinal (Flow)
-40°C to
ASTM E831
°C
2
Coefficient of Linear Expansion (CLTE) Longitudinal (Flow)
-40°C to
ISO 11359-2
°C
2
combustion performance
Test Condition
Test Method
Unit
PA66/SABIC INNOVATIVE NANSHA/RF00AS-BK1A817
UL fire rating HB
UL94
mm
1