Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B3S BASF GERMANY
Ultramid®
Thin walled components、parts、Shell、Thin walled components、parts、Shell
crystallization、High mobility、Fast forming cycle、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3S
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
275°C/5.0kg
ISO1133
cm3/10min
1
Water absorption rate
饱和,23°C
ISO62
%
9
Water absorption rate
平衡,23°C,50%RH
ISO62
%
3
Mechanical performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3S
Nominal tensile fracture strain
23°C
ISO527-2
%
1
Tensile modulus
23°C
ISO527-2
Mpa
3
Tensile strain
屈服,23°C
ISO527-2
%
4
Tensile stress
屈服,23°C
ISO527-2
Mpa
9
Bending modulus
23°C
ISO178
Mpa
3
Thermal performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3S
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
6
Melting temperature (DSC)
ISO3146
°C
2
Electrical performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3S
Leakage Trace Index
IEC60112
V
6
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3S
Charpy Notched Impact Strength
-30°C
ISO179
kJ/m²
3
Charpy Notched Impact Strength
23°C
ISO179
kJ/m²
4
Impact strength of simply supported beam without notch
-30°C
ISO179
kJ/m²
2
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
2
Impact strength of cantilever beam gap
-30°C
ISO180
kJ/m²
3
Impact strength of cantilever beam gap
23°C
ISO180
kJ/m²
4
hardness
Test Condition
Test Method
Unit
PA6/BASF GERMANY/B3S
Ball pressure hardness
ISO2039-1
Mpa
1