PEEK A2000 BASF GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PEEK/BASF GERMANY/A2000
Molding shrinkage rate
ASTM D955
%
5
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
3
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
3
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEEK/BASF GERMANY/A2000
elongation at break
ASTM D638/ISO 527
%
2
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
elongation
ASTM D638/ISO 527
%
5
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
7
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
2
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
5
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
3
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
5
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
3
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
2
Thermal performance
Test Condition
Test Method
Unit
PEEK/BASF GERMANY/A2000
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
3
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
3
vicat softening point
ASTM D1525/ISO R306
℃（℉）
1
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
0
Electrical performance
Test Condition
Test Method
Unit
PEEK/BASF GERMANY/A2000
Surface resistivity
ASTM D257/IEC 60093
Ω
>