PC/PBT X2420 BK1066 SABIC INNOVATIVE NANSHA
XENOY™
Automotive Applications
High mobility、High impact resistance、Dimensional stability、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/X2420 BK1066
Melt volume flow rate
265°C/2.16kg
ISO1133
cm3/10min
1
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
2
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
TD:3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/X2420 BK1066
crack
ISO527-2/5
%
7
crack
ISO527-2/5
Mpa
3
Fracture 3
ASTMD638
Mpa
3
Tensile modulus 1
ASTMD638
Mpa
3
yield
ISO527-2/5
Mpa
5
yield
ISO527-2/5
%
3
Surrender 2
ASTMD638
Mpa
5
Surrender 4
ASTMD638
%
3
Bending modulus 5
50.0mm跨距
ASTMD790
Mpa
3
Bending strength 6
屈服,50.0mm跨距
ASTMD790
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/X2420 BK1066
RTI
UL746
°C
7
RTIElec
UL746
°C
7
Evolution Calendar intelligent importer
UL746
°C
7
Horizontal: 23 to 80 ° C
ISO11359-2
cm/cm/°C
9
Horizontal: -40 to 40 ° C
ASTME831
cm/cm/°C
8
Flow: 23 to 80 ° C
ISO11359-2
cm/cm/°C
4
Flow: -40 to 40 ° C
ASTME831
cm/cm/°C
5
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Vicat softening temperature
ISO306/B120
°C
1
Impact performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE NANSHA/X2420 BK1066
23°C
ASTMD256
J/m
2
23°C
ASTMD4812
J/m
1
23°C10
ISO180/1A
kJ/m²
1
23°C12
ISO180/1U
kJ/m²
1
-30°C11
ISO180/1U
kJ/m²
7
-30°C9
ISO180/1A
kJ/m²
8
Impact strength of simply supported beam gap 7
23°C
ISO179/1eA
kJ/m²
1
Impact strength of simply supported beam gap 7
-30°C
ISO179/1eA
kJ/m²
7
Simple supported beam without notch impact strength 8
-30°C
ISO179/1eU
kJ/m²
9
Simple supported beam without notch impact strength 8
23°C
ISO179/1eU
kJ/m²
9
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
3