Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA CR7500 BK1041 SABIC INNOVATIVE SHANGHAI
GELOY™
Electrical applications、Automotive Applications
Thermal stability、Antistatic、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE SHANGHAI/CR7500 BK1041
Melt flow rate
220°C/10.0 kg
ASTM D1238
g/10 min
6
Melt flow rate
260°C/5.0 kg
ASTM D1238
g/10 min
1
Molten Volume Flow Rate (MVR)
220°C/10.0 kg
ISO 1133
cm3/10min
6
Molten Volume Flow Rate (MVR)
260°C/5.0 kg
ISO 1133
cm3/10min
1
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE SHANGHAI/CR7500 BK1041
Tensile strength
屈服 3
ASTM D638
Mpa
4
Tensile strength
屈服
ISO 527-2/5
Mpa
4
Tensile strength
断裂 3
ASTM D638
Mpa
3
Tensile strength
断裂
ISO 527-2/5
Mpa
3
Tensile modulus
-- 2
ASTM D638
Mpa
1
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 3
ASTM D638
%
3
elongation
屈服
ISO 527-2/5
%
3
elongation
断裂 3
ASTM D638
%
6
elongation
断裂
ISO 527-2/5
%
1
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
Bending stress
-- 5, 6
ISO 178
Mpa
6
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE SHANGHAI/CR7500 BK1041
Vicat softening temperature
--
ASTM D152510
°C
9
Vicat softening temperature
--
ISO 306/B50
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831, ISO 11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
9
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
9
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
9
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9
ISO 75-2/Ae
°C
8
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
ISO 75-2/Af
°C
8
Impact performance
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE SHANGHAI/CR7500 BK1041
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
3