Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP G3220A 10000 SABIC INNOVATIVE US
SABIC®
Engine hood parts、Automotive sector
Homopolymer、Chemical coupling
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PP/SABIC INNOVATIVE US/G3220A 10000
Melt mass flow rate
230°C/2.16kg
ISO1133
g/10min
1
Mechanical performance
Test Condition
Test Method
Unit
PP/SABIC INNOVATIVE US/G3220A 10000
Tensile strength
断裂3
ASTMD638
Mpa
8
Tensile strength
断裂
ISO527-2/1A/50
Mpa
8
Tensile modulus
--2
ASTMD638
Mpa
5
Tensile modulus
--
ISO527-2/1
Mpa
4
elongation
断裂3
ASTMD638
%
3
elongation
断裂
ISO527-2/50
%
3
Bending modulus
50.0mm跨距4
ASTMD790
Mpa
4
Bending modulus
64.0mm跨距5
ISO178
Mpa
4
Thermal performance
Test Condition
Test Method
Unit
PP/SABIC INNOVATIVE US/G3220A 10000
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,未退火6
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火6
ISO75-2/A
°C
1
Vicat softening temperature
ISO306/A50
°C
1
Linear coefficient of thermal expansion
MD:-30到100°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD:-30到100°C
ISO11359-2
cm/cm/°C
1
Impact performance
Test Condition
Test Method
Unit
PP/SABIC INNOVATIVE US/G3220A 10000
Cantilever beam without notch impact strength 8
23°C,3.20mm
ASTMD4812
J/m
6
Dart impact equipped with measuring instruments 9
23°C,EnergyatPeakLoad
ASTMD3763
J
7