Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT X2500UV-YW8E099 SABIC INNOVATIVE US
XENOY™
Electronic and electrical、Automotive components
High impact、No fill
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X2500UV-YW8E099
Melt volume flow rate
265°C/1.2kg
ISO1133
cm3/10min
4
Melt mass flow rate
265°C/2.16kg
ASTMD1238
g/10min
9
Shrinkage rate
MD3
内部方法
%
0
Shrinkage rate
MD:3.20mm
内部方法
%
0
Shrinkage rate
TD3
内部方法
%
0
Shrinkage rate
TD2
内部方法
%
0
Shrinkage rate
MD2
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X2500UV-YW8E099
Tensile strength
屈服
ASTMD638
Mpa
5
Tensile strength
屈服5
ASTMD638
Mpa
5
Tensile strength
屈服
ISO527-2/50
Mpa
5
Tensile strength
断裂5
ASTMD638
Mpa
5
Tensile strength
断裂
ISO527-2/50
Mpa
5
Tensile strength
断裂4
ASTMD638
Mpa
5
Tensile strength
屈服4
ASTMD638
Mpa
5
Tensile modulus
--3
ASTMD638
Mpa
2
Tensile modulus
--4
ASTMD638
Mpa
2
Tensile modulus
--
ISO527-2/1
Mpa
2
elongation
屈服4
ASTMD638
%
5
elongation
断裂4
ASTMD638
%
8
elongation
屈服
ASTMD638,ISO527-2/50
%
5
elongation
屈服5
ASTMD638
%
5
elongation
断裂
ASTMD638
%
1
elongation
断裂5
ASTMD638
%
8
elongation
断裂
ISO527-2/50
%
7
Taber abraser
1000Cycles,1000g,CS-17转轮
内部方法
mg
2
Bending modulus
50.0mm跨距5
ASTMD790
Mpa
2
Bending modulus
--6
ISO178
Mpa
2
Bending modulus
--
ASTMD790
Mpa
2
Bending modulus
50.0mm跨距6
ASTMD790
Mpa
2
Bending modulus
--7
ISO178
Mpa
2
bending strength
--
ASTMD790
Mpa
7
bending strength
--7,8
ISO178
Mpa
8
bending strength
屈服,50.0mm跨距6
ASTMD790
Mpa
7
bending strength
--6,7
ISO178
Mpa
8
bending strength
屈服,50.0mm跨距5
ASTMD790
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X2500UV-YW8E099
thermal conductivity
ISO8302
W/m/K
0
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距10
ISO75-2/Af
°C
1
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距11
ISO75-2/Af
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,未退火,64.0mm跨距10
ISO75-2/Bf
°C
1
Hot deformation temperature
0.45MPa,未退火,64.0mm跨距11
ISO75-2/Bf
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Vicat softening temperature
--
ISO306/A50
°C
1
Vicat softening temperature
--
ASTMD152512,ISO306/B5012
°C
1
Vicat softening temperature
--
ASTMD152511,ISO306/B5011
°C
1
Linear coefficient of thermal expansion
TD:23到80°C
ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831
cm/cm/°C
8
Linear coefficient of thermal expansion
MD:23到80°C
ISO11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X2500UV-YW8E099
Surface resistivity
IEC60093
ohms
>
Dielectric strength
3.20mm,在油中
IEC60243-1
KV/mm
1
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X2500UV-YW8E099
Impact strength of simply supported beam gap 8
-30°C
ISO179/1eA
kJ/m²
3
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
5
Impact strength of simply supported beam gap 9
-30°C
ISO179/1eA
kJ/m²
3
Impact strength of simply supported beam gap 9
23°C
ISO179/1eA
kJ/m²
5
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
6
hardness
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X2500UV-YW8E099
Ball pressure hardness
H358/30
ISO2039-1
Mpa
9
flammability
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X2500UV-YW8E099
Burning wire flammability index
2.7mm
IEC60695-2-12
°C
7